ISO 24284-2022 pdf free download – Metallic coatings — Corrosion test method for decorative chrome plating under a de-icing salt environment.
This document specifies the apparatus, reagents, and procedure to assess the corrosion resistanceof chromium electroplated parts in the presence of de-icing salts (especially calcium chloride) in thelaboratory.
This method is primarily applicable to decorative parts plated with chromium, especially to exterior(automobile) parts electroplated with nickel-chromium or copper-nickel-chromium.
This document simulates a special corrosion in the presence of hygroscopic and corrosive de-icing saltand conductive mud with a high salt concentration on chromium electroplated deposits during winter.
2Normative references
The following documents are referred to in the text in such a way that some or all of their contentconstitutes requirements of this document. For dated references, only the edition cited applies. Forundated references, the latest edition of the referenced document(including any amendments) applies.
ISO 3696, Water for analytical laboratory use —Specification and test methods
3Terms and definitions
For the purposes of this document, the following terms and definitions apply.
IlS0 and lEC maintain terminology databases for use in standardization at the following addresses:-ISO Online browsing platform: available at https://www.iso.org/obp
—IEC Electropedia: available at https://www.electropedia.org/3.1
de-icing salt
chemical sprayed to control ice and snow on the roads
EXAMPLE Sodium chloride (rock salt), calcium chloride, and magnesium chloride.
4 Apparatus
4.1The apparatus shall consist of a humidity chamber, specimen supports, provision for heatingthe chamber, and provision for air circulation in the chamber.The humidity chamber shall maintainconstant temperature (60 °C± 3°C) and humidity (30 %±5 %).
4.2The design shall be such that drops of moisture (possibly accumulating on the roof or walls of thechamber, or on the specimen supports) do not fall on the test specimens.
4.3The construction materials shall not affect the test.
Place the test piece horizontally into a humidity chamber without spilling over the slurry.The humiditychamber shali be set at constant temperature (60 C± 3 °C) and humidity (30 % ± 5 % RH) for thetest period.The period of test and the number of test specimens shall be specified and agreed upon bythe requestor and the laboratory prior to the start of the test.Expose completely all the test pieces tothe test environment and place them so that they do not interfere with each other. After the specifiedtesting time, take out the test piece from the humidity chamber. Clean the paste using a clean soft clothor sponge under running tap water and allow it to dry using tissues, dry clothes, or an air drier.
NOTE1 Test pieces mentioned in this clause include not only sample test pieces but also real components.NOTE2 Agraphic representation of the procedure for the de-icing salt corrosion test is given in AnnexA.
7Evaluation of the results
The criteria for the evaluation of the test results shall be given in the specifications of the coating orproduct tested.
In a typical application of this test, the tested area is inspected under 10x magnification and theobserved appearance defects are assessed.An example of a typical evaluation method is given inAnnex B.
8Test report
Unless otherwise prescribed in the specifications, the test report shall contain the followinginformation:
a) a specification of the plating type, the thickness of each layer, the type of chromium layer;b)the number of test specimens;
cthe preparation method used for the test specimens;d) the method used to clean the specimens after the test;
e) the temperature and relative humidity inside the humidity chamber;f)the exposure period;
g) photographs of different areas of the specimens (at 10x magnification) taken before and after the test.ISO 24284 pdf download.